Post-fire Behaviour of Innovative Shear Connection for Steel-Concrete Composite Structures. (February 2017)

• Record Type: Journal Article
• Authors: Mashiri, Fidelis R.; Mirza, Olivia; Canuto, Carlo; Lam, Dennis
• Is Part Of: Structures. Volume 9(2017)
• Page Start: 147
• Page End: 156
• Publication Date: 2017-02
• Subjects: Composite steel-concrete -- Shear connectors -- Post-fire behaviour -- Experimental studies; Structural engineering -- Periodicals; 624.1
• DOI: 10.1016/j.istruc.2016.12.001
• Languages: English
• ISSNs: 2352-0124

Abstract

Abstract: Steel-concrete composite structures are commonly used in buildings and bridges because it takes advantage of tensile strength of steel and compressive strength of concrete. The two components are often secured by shear connectors such as headed studs to prevent slippage and to maintain composite action. In spite of its popularity, very little research was conducted on steel-concrete composites particularly on headed stud shear connectors in regards to its post-fire behaviour. This research investigates the post-fire behaviour of innovative shear connectors for composite steel and concrete. Three types of connectors were investigated. They are conventional headed stud shear connectors, Blind Bolt 1 and Blind Bolt 2 blind bolts. Push-out test experimental studies were conducted to look at the behaviour and failure modes for each connector. Eighteen push tests were conducted according to Eurocode 4. The push test specimens were tested under ambient temperatures and post-fire condition of 200 °C, 400 °C and 600 °C. The results in ambient temperature are used to derive the residual strength of shear connectors after exposing to fire. This research showed that the headed studs performed well compared to Blind Bolts 1 and 2 at ambient and target temperatures. The stress concentrations around the casing of Blind Bolt 1 were found to cause a reduction in strength of the specimens. Findings from this research will provide fundamental background in designing steel-concrete composites where there is danger of fire exposure.