Solidification mechanism and microstructure evolution of Al2O3-ZrO2 ceramic coating prepared by combustion synthesis and thermal explosion spraying. Issue 5 (1st April 2017)

• Record Type: Journal Article
• Authors: Pan, Jiayu; Zheng, Yongting; Zheng, Yuandi; Ye, Wei; Yu, Wanjun
• Is Part Of: Ceramics international. Volume 43:Issue 5(2017)
• Page Start: 4037
• Page End: 4041
• Publication Date: 2017-04-01
• Subjects: Microstructure evolution -- Rapid solidification -- Al2O3/ZrO2 -- Ultra-fined ceramic coating; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2016.11.153
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: The solidification mechanism and microstructure of the hypoeutectic Al2 O3 -ZrO2 (Al2 O3 :72 mol%) ultra-fined ceramic coating prepared by combustion synthesis and rapid plate cooling method were analyzed by the heat transfer process and dynamic characteristics. The rapid solidification process inhibited the transformation from the t-ZrO2 to m-ZrO2 at low temperatures. The growth rate of the solid-liquid interface to form the amorphous and nano-crystalline Al2 O3 -ZrO2 was about 65.7 mm/s and 13.7 mm/s, respectively. The mechanism formation of both the amorphous and nano-crystalline areas were analyzed using rapid solidification models. When the growth rate reduced to about 8.23 mm/s, large quantities of nanosized eutectic structures was identified by SEM in the pseudo-eutectic area. The interphase spacing of the eutectic structures was 40–100 nm. In addition, some typical divorced eutectic structures appeared at this area. After that, micron dendrites (0.2–0.6 µm) took the main part when the growth rate decreased to about 3.67 mm/s for such a hypoeutectic Al2 O3 -ZrO2 binary system. The nano-crystalline area showed the highest nanohardness (22 GPa). This paper may provide new guidance to prepare high performance Al2 O3 -ZrO2 ceramics both in experiment and theory.