Controlled synthesis and electromagnetic wave absorption properties of core-shell Fe3O4@SiO2 nanospheres decorated graphene. Issue 2 (1st February 2017)

• Record Type: Journal Article
• Authors: Wang, Yanping; Lai, Yaru; Wang, Suyun; Jiang, Wei
• Is Part Of: Ceramics international. Volume 43:Issue 2(2017)
• Page Start: 1887
• Page End: 1894
• Publication Date: 2017-02-01
• Subjects: Fe3O4@SiO2/RGO nanocomposite -- Magnetic properties -- Electromagnetic wave absorption -- Reflection loss; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2016.10.148
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Fe3 O4 /reduced graphene oxide (RGO) nanocomposite was synthesized by a simple hydrothermal method and then SiO2 coated onto Fe3 O4 by a modified Stӧber method. The transmission electron microscopy and field emission scanning electron microscopy characterization indicate that masses of Fe3 O4 @SiO2 core-shell structure nanospheres attached to the RGO sheets, and that the thicknesses of SiO2 shells are about 20–40 nm. The X-ray diffractograms and Raman spectra illustrate that the synthesized samples consist of highly crystallized cubic Fe3 O4, amorphous SiO2 and disorderedly stacked RGO sheets. The magnetic hysteresis loops reveal the ferromagnetic behavior of the samples at room temperature. In addition, the Fe3 O4 @SiO2 /RGO paraffin composite exhibit excellent electromagnetic wave absorption properties at room temperature in the frequency range of 2–18 GHz, which are attributed to the effective complementarities between the dielectric loss and magnetic loss. For Fe3 O4 @SiO2 /RGO-1 and Fe3 O4 @SiO2 /RGO-2 nanocomposite, the minimum reflection loss can reach −26.4 dB and −16.3 dB with the thickness of 1.5 mm, respectively. The effective absorption bandwidth of the samples can reach more than 10.0 GHz with the thickness in the range of 1.5–3.0 mm. It is demonstrated that such nanocomposite could be used as a promising candidate in electromagnetic wave absorption area.