POSS–PU electrospinning nanofibers membrane with enhanced blood compatibility. Issue 70 (11th July 2016)

• Record Type: Journal Article
• Authors: Song, Xiaoyan; Li, Tao; Cheng, Bowen; Xing, Jinfeng
• Is Part Of: RSC advances. Volume 6:Issue 70(2016)
• Page Start: 65756
• Page End: 65762
• Publication Date: 2016-07-11
• Subjects: Chemistry -- Periodicals; 540.5
• DOI: 10.1039/c6ra07681e
• Languages: English
• ISSNs: 2046-2069

Abstract

Abstract : The addition of POSS results in (a) platelet adsorption amount of electrospun fibers membrane decreased (b) protein adsorption of electrospun fibers membrane decreased (c) the growth of bacteria was inhibited. Abstract : Open cage polyhedral oligomeric silsesquioxane (POSS) was firstly used to modify polyurethane (PU) to prepare a POSS–PU composite. Then a POSS–PU nanofiber membrane was prepared by electrospinning technology. The hydrophilic/hydrophobic properties, fiber morphology and biocompatibility of the POSS–PU nanofibers membrane were investigated. Contact angle increased by 24.3° for 2 wt% POSS–PU nanofibers membrane compared to PU. The ability of the nanofibers membrane surface to repel proteins and platelets was assessed by using platelet adhesion test and BSA static protein-adsorption experiment. Platelet adsorption amount obviously decreased compared with PU and very few platelet was adhered on the surfaces of nanofibers membranes when 1 wt% POSS was added. Protein adsorption was also decreased with addition of POSS. Hemolysis tests showed that hemolysis rate localized in the desired range of values (<5%) for all nanofibers membrane. Moreover, the antibacterial activity of nanofibers membranes was obviously improved after addition of POSS.