Development of a neutral cementitious material to promote vegetation concrete. (30th November 2016)

• Record Type: Journal Article
• Authors: Lee, Kyung-Ho; Yang, Keun-Hyeok
• Is Part Of: Construction & building materials. Volume 127(2016)
• Page Start: 442
• Page End: 449
• Publication Date: 2016-11-30
• Subjects: Neutral binder -- Vegetation concrete -- Alpha-calcium sulfate hemihydrate -- Portlandite -- Ph; Building materials -- Periodicals; 624.18
• DOI: 10.1016/j.conbuildmat.2016.10.032
• Languages: English
• ISSNs: 0950-0618

Abstract

Highlights: A neutral binder using alpha-calcium sulfate hemihydrate (α-CH) was developed. The mass fraction of Ca(OH)2 was found to be approximately 11% of cement content. The microstructural characteristics and strength gain of α-CH were established. The use of cement is impractical for reducing the alkalinity of concrete. The developed α-CH binders possesses potential for production of vegetation concrete. Abstract: To develop a neutral binder for vegetation concrete, various cementitious materials based on alpha-calcium sulfate hemihydrate (α-CH) were compositionally examined as follows: 25% and 50% of the α-CH content were partially replaced by a mineral admixture; and 25%, 50%, 75%, and 100% were replaced by ordinary portland cement (OPC). The hydration products and microstructural characteristics of the prepared binders were investigated using X-ray diffraction analysis and scanning electron microscopy. The portlandite [Ca(OH)2 ] phase formed in the hydrated cementitious materials was quantified by thermogravimetric analysis to examine the relationship between Ca(OH)2 content and pH values of the pastes. The OPC paste without α-CH showed several diffraction peaks for the Ca(OH)2 phase, whereas the α-CH paste had no diffraction peak at the angles corresponding to Ca(OH)2 . The dehydration mass fraction of Ca(OH)2 corresponded to approximately 11% of the cement content included in each paste sample. The 28-day compressive strength of α-CH mortar was approximately 55% of that of OPC mortar, whereas the α-CH-based pastes without OPC maintained the pH at the neutral level, between 6.5 and 6.9, showing that the use of cement, even in very low amounts, is impractical for reducing the alkalinity of concrete. The α-CH possesses significant potential for practical production of neutral vegetation concrete.