Large Persistent Photoconductivity in Strontium Titanate at Room Temperature. Issue 1792 (28th May 2015)

• Record Type: Journal Article
• Authors: Poole, Violet M.; Dashdorj, J.; Zvanut, Mary Ellen; McCluskey, Matthew D.
• Editors: Herrick, R.; Miyake, H.; Palacios, T.; Shiojima, K.; Ueda, O.; Chen, Y.; Liliental-Weber, Z.; Narayan, J.; Weber, E.R.
• Is Part Of: MRS proceedings. Issue 1792(2015)
• Publication Date: 2015-05-28
• Subjects: defects, -- oxide, -- photoconductivity; Electrical engineering -- Congresses; Physics -- Congresses; Materials -- Research -- Congresses; Materials science -- Congresses; 620.11
• DOI: 10.1557/opl.2015.531
• Languages: English
• ISSNs: 0272-9172

Abstract

ABSTRACT: Strontium titanate (SrTiO3 ) is a wide-band-gap semiconductor with a variety of novel properties. In this work, bulk single crystal SrTiO3 samples were heated to 1200°C, resulting in the creation of point defects. These thermally treated samples showed large persistent photoconductivity (PPC) at room temperature. Illumination with sub-gap light (>2.9 eV) caused an increase in free-electron concentration by over two orders of magnitude. After the light is turned off, the conductivity persists at room temperature, with essentially zero decay over several days. The results of electron paramagnetic resonance (EPR) measurements suggest that a point defect is responsible for PPC because the photo-induced response of one of the EPR signals is similar to that seen for the PPC. Due to a large barrier for recapture, the photo-excited electron remains in the conduction band, where it contributes to the conductivity.