A green fabrication strategy for porous Yb3Al5O12 ceramics with high strength and tunable gas permeability. Issue 19 (13th September 2016)

• Record Type: Journal Article
• Authors: Wang, Xiaofei; Xiang, Huimin; Wang, Guigen; Zhou, Yanchun
• Is Part Of: Journal of materials research. Volume 31:Issue 19(2016)
• Page Start: 3078
• Page End: 3087
• Publication Date: 2016-09-13
• Subjects: ceramic, -- porosity, -- sintering; Materials -- Research -- Periodicals; 620.1105
• DOI: 10.1557/jmr.2016.319
• Languages: English
• ISSNs: 0884-2914

Abstract

Abstract: Abstract : Novel porous Yb3 Al5 O12 ceramics are successfully fabricated via a green and simple foam-gelcasting approach. Using a nontoxic water-soluble copolymer of isobutylene and maleic anhydride (Isobam), together with a surfactant EMAL TD (Surf-E), 50 vol% solid loading Yb3 Al5 O12 aqueous ceramic slurries are prepared. Thanks to the small contents of organic additives (0.4 wt% Isobam and 1 vol% Surf-E) added, low linear shrinkage (∼13.9%), and mass loss (∼2.21 wt%) are obtained after pressureless sintering of gelcasted green body at 1600 °C for 4 h under an air atmosphere. Furthermore, porous Yb3 Al5 O12 ceramics with controlled porosity and spherical-like cells possess excellent structural and shape stability. The flexural strength and compressive strength of the as-prepared porous Yb3 Al5 O12 ceramics with a relative density of 20% remain as high as 6.3 and 19.7 MPa, respectively, and the gas permeability can be tuned between 4.3 × 10 −13 and 7.8 × 10 −11 m 2 with exponentially increasing porosity from 58% to 84%.