Facile synthesis of N-doped carbon-coated Si/Cu alloy with enhanced cyclic performance for lithium ion batteries. Issue 81 (16th August 2016)

• Record Type: Journal Article
• Authors: Deng, Libo; Zhang, Wei; Ren, Xiangzhong; Zhang, Peixin; Li, Yongliang; Sun, Lingna; Gao, Yuan
• Is Part Of: RSC advances. Volume 6:Issue 81(2016)
• Page Start: 78100
• Page End: 78105
• Publication Date: 2016-08-16
• Subjects: Chemistry -- Periodicals; 540.5
• DOI: 10.1039/c6ra15847a
• Languages: English
• ISSNs: 2046-2069

Abstract

Abstract : Nanoparticles consisting of silicon/copper/nitrogen-doped-carbon (Si/Cu/N–C) with a Si/Cu alloy core and a N–C shell have been prepared and their cyclic life as an anode in lithium-ion batteries was significantly enhanced compared to Si/Cu alloy. Abstract : Nanoparticles consisting of silicon/copper/nitrogen-doped-carbon (Si/Cu/N–C) with a Si/Cu alloy core and a N–C shell have been synthesized by a two-step process, including the preparation of a Si/Cu alloy via mechanical ball milling and the preparation of Si/Cu/polydopamine (PDA) through in situ polymerization of dopamine followed by carbonization at 850 °C. Their microstructures and their electrochemical performance as an anode in lithium-ion batteries (LIB) were investigated. The composite nanoparticles show a coulomb efficiency of 74% in the first cycle and a discharge capacity of 851 mA h g −1 in the second cycle. They still retain 89% of their second-cycle capacity after 100 cycles at a current density of 0.08 mA cm −2 . These results are superior to those for a Si/Cu alloy without the carbon coating, which is thought to be due to the carbon layer being able to mitigate the volume change of silicon and the nitrogen-doping can further enhance the wettability and electrical conductivity of the electrode material.