Three‐dimensional in vitro measurements of tooth wear using fluoridated dentifrices. (September 2016)

• Record Type: Journal Article
• Authors: Al‐Mashhadani, A; Plygkos, I; Bozec, L; Rodriguez, JM
• Is Part Of: Australian dental journal. Volume 61:Number 3(2016:Sep.)
• Page Start: 304
• Page End: 309
• Publication Date: 2016-09
• Subjects: Abrasion -- erosion -- surface matching -- three‐dimensional -- two‐dimensional; Dentistry -- Periodicals; Dentistry -- Periodicals; Dentisterie -- Australie -- Périodiques; Tandheelkunde; 617.6
• DOI: 10.1111/adj.12372
• Languages: English
• ISSNs: 0045-0421

Abstract

Abstract: Background: The aim of this study was to compare differences in wear of human enamel and dentine in vitro using a 3D measurement method comparing silica versus non‐silica containing fluoridated dentifrices (Colgate Total ™ [CT] or Fluor Protector Gel ™ [FPG]). Methods: Mounted native enamel (n = 36) and polished dentine (n = 36) samples were subjected to 10 wear cycles. Each cycle consisted of: (1) 1 hour remineralization in artificial saliva (AS); (2) 10 minute erosion (0.3% citric acid; pH = 2.8); (3) 2 minute toothbrush abrasion in AS (G1, control) or a slurry of 3:1 by weight of AS:dentifrice (G2 = CT; G3 = FPG) under a load of 2 N. Each group contained 12 enamel and 12 dentine samples. Paired pre‐ and post‐wear scans made with a contacting scanner were digitally superimposed using ball bearings as datum. Results: Mean and (SD) enamel wear was G1 = 21.9 μm (6.4); G2 = 15.2 μm (2.8); G3 = 16.9 μm (3.2). Enamel wear was not different between dentifrices (p = 0.99). Both dentifrices resulted in less enamel wear compared to the control (p < 0.05). Dentine wear was G1 = 41.3 μm (8.1); G2 = 29.1 μm (4.4); G3 = 22.1 μm (3.5). Differences in measurements were observed between dentifrices and control (p < 0.05) and between dentifrices (p = 0.014) with FPG showing less dentine wear than CT. Conclusions: FPG offered protection against erosive/abrasive tooth wear in dentine compared to CT. FPG did not offer such protective effect on enamel wear.