Catalytic hydrotreatment of fast pyrolysis liquids in batch and continuous set-ups using a bimetallic Ni–Cu catalyst with a high metal content. Issue 15 (19th May 2016)

• Record Type: Journal Article
• Authors: Yin, Wang; Kloekhorst, Arjan; Venderbosch, Robertus H.; Bykova, Maria V.; Khromova, Sofia A.; Yakovlev, Vadim A.; Heeres, Hero J.
• Is Part Of: Catalysis science & technology. Volume 6:Issue 15(2016)
• Page Start: 5899
• Page End: 5915
• Publication Date: 2016-05-19
• Subjects: Catalysis -- Periodicals; 541.395
• DOI: 10.1039/c6cy00503a
• Languages: English
• ISSNs: 2044-4753

Abstract

Abstract : In this paper, the effects of process conditions on catalyst performance and product properties are reported in both batch and continuous set-ups. Abstract : In this paper, an experimental study on the hydrotreatment of fast pyrolysis liquids is reported in both batch and continuous set-ups using a novel bimetallic Ni–Cu based catalyst with high Ni loading (up to 50%) prepared by a sol–gel method. The experiments were carried out in a wide temperature range (80–410 °C) and at a hydrogen pressure between 100–200 bar to determine product properties and catalyst performance as a function of process conditions. To gain insight into the molecular transformations, the product oils were analysed by GC × GC, 1 H-NMR and GPC and reveal that the sugar fraction is reactive in the low temperature range (<200 °C), whereas the lignin fraction is only converted at elevated temperatures (>300 °C). In addition, the organic acids are very persistent and reactivity was only observed above 350 °C. The results are rationalized using a reaction network involving competitive hydrogenation of reactive aldehydes and ketones of the sugar fraction of fast pyrolysis liquids and thermal polymerisation. In addition, relevant macro-properties of the product oils including flash point (30 to 80 °C), viscosity (0.06 to 0.93 Pa s) and TG residue (<1 to about 8 wt%) were determined and compared. Product oils with the lowest oxygen content (<13 wt%) were obtained in the continuous set-up at 410 °C.