Fabrication and Property of Mullite Whiskers Frameworks with an Ultrahigh Porosity by Expandable Mesocarbon Microbeads. Issue 7 (26th May 2016)

• Record Type: Journal Article
• Authors: Zeng, De‐Jun; Zhang, Ya‐Ming; Yang, Jian‐Feng; Wang, Bo; Matsushita, Junichi
• Editors: Ferreira, J.
• Is Part Of: Journal of the American Ceramic Society. Volume 99:Issue 7(2016)
• Page Start: 2226
• Page End: 2228
• Publication Date: 2016-05-26
• Subjects: mullite -- porous materials -- strength -- whiskers; Ceramics -- Periodicals; 620.1405
• DOI: 10.1111/jace.14309
• Languages: English
• ISSNs: 0002-7820

Abstract

Abstract : Mullite whiskers frameworks with an ultrahigh porosity were fabricated by the vapor‐phase reaction of AlF3, Al2 O3, and SiO2 and adding expandable mesocarbon microbeads (MCMB) as a pore‐forming agent. A large volume expansion of 122% for MCMB due to its layered structure occurred during the formation of mullite whiskers, resulting in the expansion of samples and high porosities of 87.7%–98.2% at 50–90 wt% MCMB contents. Perfect whiskers and a lap‐joint structure formed due to the formation of mullites through the vapor‐phase reaction. A bimodal pore structure was achieved from the spaces of the whiskers framework and burning of the expanded MCMB. High compressive strengths of 1.7 to 5.4 MPa were obtained for the porous mullite at porosities of 94.2%–87.7%, which suggested a rigid structure; these strengths at the ultrahigh porosities are attributed to the merit of the framework with high strength whiskers and their strong bonding.