The Effect of Thermal Exposure on the Microstructures and Mechanical Properties of 2198 Al–Li Alloy. Issue 7 (9th March 2016) - Chen, Bin
Abstract : The effect of thermal exposure on the microstructure and mechanical properties of 2198 Al–Li alloy is investigated. It is found that thermal exposure will lead to deterioration of the strengths, except the one exposed at 200 °C. When exposure temperature increases to 300 °C, a dramatical drop in strength and a rise in ductility appear due to the dissolution of strengthening phases, T1 phase, and θ′ phase. The new phases, (Al2 Cu), Al6 Cu(Li, Mg)3, and Al6 CuLi3 phases, are formed. Compared with the alloy exposed at 300 °C, the alloys exposed at 400 and 500 °C exhibit better mechanical properties due to the precipitation of δ′ phase. The fractographic observation shows that the predominant fracture mode changes from quasi‐cleavage fracture to ductile fracture with the increasing exposure temperature. Abstract : A commercial sheet of 2198‐T8 alloy is subjected to thermal exposure at elevated temperatures varying from 200 to 500 °C . Thermal exposure at 200 °C leads to deterioration of the ductility while thermal exposure at 300 °C and above leads to deterioration of the strengths. It is mainly due to the phase transition during thermal exposure.