Ferroelectric polymer nanopillar arrays on flexible substrates by reverse nanoimprint lithography. Issue 25 (3rd June 2016)

• Record Type: Journal Article
• Authors: Song, Jingfeng; Lu, Haidong; Foreman, Keith; Li, Shumin; Tan, Li; Adenwalla, Shireen; Gruverman, Alexei; Ducharme, Stephen
• Is Part Of: Journal of materials chemistry. Volume 4:Issue 25(2016)
• Page Start: 5914
• Page End: 5921
• Publication Date: 2016-06-03
• Subjects: Materials -- Periodicals; Chemistry, Analytic -- Periodicals; Optical materials -- Research -- Periodicals; Electronics -- Materials -- Research -- Periodicals; 543.0284
• DOI: 10.1039/c6tc01848c
• Languages: English
• ISSNs: 2050-7526

Abstract

Abstract : Large area ferroelectric polymer nanopillar arrays were prepared directly on flexible substrates using soft-mold reverse nanoimprint lithography at low pressure. Abstract : With the increasing interest in deploying ferroelectric polymer in flexible electronics and electro-mechanics, high-throughput and low-cost fabrication of 3D ferroelectric polymer nanostructures on flexible substrates can be a significant basis for future research and applications. Here, we report that large arrays of ferroelectric polymer nanopillars can be prepared directly on soft, flexible substrates by using low-cost polydimethylsiloxane (PDMS) soft-mold reverse nanoimprint lithography at 135 °C and at pressures as low as 3 bar. The nanopillar arrays were highly uniform over large areas of at least 200 × 200 μm and had good crystallinity with nearly optimum (110) orientation. Furthermore, the method leaves little or no residual polymer layer, fully isolating the nanopillars to avoid cross-talk and, obviating the need for additional etching processes that arises with conventional low-contrast nanoimprinting. The ferroelectric properties of individual nanopillars were probed by piezoresponse force microscopy, which showed that they exhibited switchable and bi-stable polarization. In addition, the polarization hysteresis loops probed by pyroelectric measurements of the entire array showed that the nanopillar capacitor arrays had good ferroelectric switching characteristics, over areas of at least 1 mm × 1 mm.