Effect of Graphitization on the Microstructure and Properties of Mo2C‐Modified C/C–Cu Composites1 . Issue 6 (12th December 2015)

• Record Type: Journal Article
• Authors: Zhou, Wen Yan; Peng, Ke; Ran, Li Ping; Ge, Yi Cheng; Yi, Mao Zhong
• Is Part Of: Advanced engineering materials. Volume 18:Issue 6(2016:Jun.)
• Page Start: 1017
• Page End: 1021
• Publication Date: 2015-12-12
• Subjects: Materials -- Periodicals; 620.11
• DOI: 10.1002/adem.201500489
• Languages: English
• ISSNs: 1438-1656

Abstract

Abstract : Carbon/carbon–copper(C/C–Cu) composites are fabricated by infiltration of Cu into Mo2 C interlayer‐modified carbon/carbon(C/C) preforms. Effect of graphitization on the microstructure and properties of the C/C–Cu composites is studied. The C/C–Cu composite with graphitization shows lower electrical resistivity, thermal expansion coefficient, friction coefficient, and an obvious higher thermal conductivity due to higher graphitization degree. However, it presents lower flexural strength, impact toughness, and higher wear rate. The composite with graphitization exhibits mainly abrasive wear while that without graphitization exhibits mainly adhesion wear, and both composites show oxidation wear. Abstract : Both the C/C preforms with and without graphitization are penetrated by Cu after modifying with Mo2 C interlayer . The C/C–Cu composite with graphitization shows better electrical and thermal conductivity, while lower strength and wear resistance. The composite with and without graphitization exhibits mainly abrasive wear and adhesion wear, respectively, and both composites show oxidation wear.