Magnetic and phonon transitions in B-site Co doped BiFeO3 ceramics. Issue 11 (15th August 2016)

• Record Type: Journal Article
• Authors: Chiang, Yueh-Sheng; Tu, Chi-Shun; Chen, Pin-Yi; Chen, Cheng-Sao; Anthoniappen, J.; Ting, Yi; Chan, Ting-Shan; Schmidt, V.H.
• Is Part Of: Ceramics international. Volume 42:Issue 11(2016)
• Page Start: 13104
• Page End: 13112
• Publication Date: 2016-08-15
• Subjects: Bi(Fe1-xCox)O3 ceramics -- Magnetic susceptibility -- Phonon -- Transition -- Superexchange; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2016.05.097
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Magnetic susceptibility and phonons have been characterized in multiferroic Bi(Fe1− x Co x )O3−δ ceramics for x =0.0, 0.05, and 0.10 (BFO100 x Co) as functions of temperature. A preferred (100) crystallographic orientation and increasing average oxygen vacancies were observed in BFO5Co and BFO10Co. The Fe and Co K-edge synchrotron X-ray absorptions revealed mixed valences of Fe 3+, Fe 4+, Co 2+, and Co 3+ ions in BFO5Co and BFO10Co, which exhibit a ferromagnetic (or ferrimagnetic) phase below room temperature due to appearance of ferromagnetic B–O–B (B=Fe and Co) superexchange interactions. Field–cooled (FC) and zero–field–cooled (ZFC) magnetic susceptibilities exhibit a significant spin-glass splitting below room temperature in BFO5Co and BFO10Co. Two Raman-active phonon anomalies at ~170 K (or 200 K) and ~260 K were attributed to the Fe 3+ –O–Co 3+ and Co 3+ –O–Co 3+ magnetic orderings, respectively. This work suggests that the low-spin Co 2+ –O–Co 2+, Fe 3+ –O–Fe 3+ (or Fe 4+ ), and high-spin Co 2+ –O–Co 2+ superexchange interactions are responsible for phonon anomalies at ~290 (or ~300 K), ~400, and ~470 K (or ~520 K) in BFO5Co and BFO10Co.