Effect of Long‐Term Thermal Aging on Microstructure and High‐Temperature Strength of a 10% Cr Martensite Ferritic Steel. Issue 5 (8th October 2015) - Gu, Tao
Abstract : The effect of long‐term thermal aging on microstructure and high‐temperature strength of a 10% Cr martensite ferritic steel is investigated. Comparison of the long‐term aging behavior at 700 °C with that at 650 °C reveals that the low angle boundary fraction increases and the coarsening of the M23 C6 carbide accelerates at higher temperature, thereby the speed of subgrain growth increases. Additionally, elevated aging temperature suppressed nucleation of Laves phases and did not affect the K‐S orientation relationship between M23 C6 carbides and ferrite matrix. The yield strength at 700 °C decreases, obviously, with increase of aging time at 700 °C, but its decline trend is not fully consistent with the change of the dislocation density, which confirms that loss of high‐temperature strength is not only due to decreasing of free dislocations. On the other hand, the variation on increasing of the subgrain width shows a similar abrupt trend to that on decreasing of the yield strength. It is suggested that for aged steel, subgrain coarsening is also an important factor for the deterioration of yield strength. Abstract : Microstructure evolution of 10% Cr steel during long‐term thermal aging is shown. And the effect of aging temperature on microstructure is studied in detail. Moreover, the correlation between microstructure and high temperature strength has been established.