Veneer Ceramic to Y‐TZP Bonding: Comparison of Different Surface Treatments. Issue 4 (21st May 2015)

• Record Type: Journal Article
• Authors: Kirmali, Omer; Kapdan, Alper; Kustarci, Alper; Er, Kursat
• Is Part Of: Journal of prosthodontics. Volume 25:Issue 4(2016)
• Page Start: 324
• Page End: 329
• Publication Date: 2015-05-21
• Subjects: Yttria‐stabilized tetragonal zirconia polycrystal (Y‐TZP) -- zirconia restorations -- veneering ceramics -- surface treatments -- dental lasers -- shear bond strength -- Er‐Cr:YSGG laser -- SEM; Prosthodontics -- Periodicals; Dental implants -- Periodicals; Dentistry -- Periodicals; 617.69
• DOI: 10.1111/jopr.12304
• Languages: English
• ISSNs: 1059-941X

Abstract

Abstract: Purpose: The purpose of this study was to evaluate the effects of various surface‐treatment techniques for enhancing the bond strength between veneering ceramic and yttria‐stabilized tetragonal zirconia polycrystals (Y‐TZP). Materials and Methods: Pre‐sintered Y‐TZP specimens were divided into eight groups (n = 10) according to the surface‐treatment technique used: (a) untreated (control); (b) air abrasion with aluminum oxide particles; (c) erbium, chromium:yttrium‐scandium‐gallium‐garnet (Er, Cr:YSGG) laser irradiation at different energy intensities (1 to 6 W). All specimens were then sintered and veneered with veneering ceramic according to the manufacturer's instructions. The obtained zirconia‐ceramic specimens were immersed in 37°C distilled water for 24 hours before a shear bond strength test using a universal testing device at a 1 mm/min crosshead speed. The average values were calculated. After debonding, the Y‐TZP surfaces were examined under a stereomicroscope to determine their fracture pattern, and the surface topography was evaluated with scanning electron microscopy after surface treatments. Results: The bond strength ranged from 13.24 to 20.54 MPa. All surface treatments increased the bond strength between the veneering ceramic and Y‐TZP; however, the value for the 6 W irradiation group was significantly different from the values for other groups ( p ˂ 0.05). Conclusions: The present study's findings showed that higher energy densities were needed for the laser irradiation to improve the bond strength between the veneering ceramic and zirconia. Clinical Implication : Y‐TZP is commonly used as a core material in fixed restorations. The bond strength between zirconia and the veneering ceramic can be affected by various surface treatments.