Piezoelectric and non-linear optical properties of α-quartz type Si1−xGexO2 single crystals. Issue 14 (17th March 2016)

• Record Type: Journal Article
• Authors: Clavier, D.; Prakasam, M.; Largeteau, A.; Boy, J. J.; Hehlen, B.; Cambon, M.; Hermet, P.; Haines, J.; Cambon, O.
• Is Part Of: CrystEngComm. Volume 18:Issue 14(2016)
• Page Start: 2500
• Page End: 2508
• Publication Date: 2016-03-17
• Subjects: Crystals -- Periodicals; Crystal growth -- Periodicals; Crystallography -- Periodicals; Cristaux -- Périodiques; Cristaux -- Croissance -- Périodiques; Cristallographie -- Périodiques; 548
• DOI: 10.1039/c5ce02477c
• Languages: English
• ISSNs: 1466-8033

Abstract

Abstract : Single crystals of α-quartz type Si1− x Ge x O2 with x < 0.2 were grown in 0.05 M NaOH solution. Abstract : Single crystals of α-quartz type Si1− x Ge x O2 with x < 0.2 were grown in 0.05 M NaOH solution. Infrared measurements confirmed that crystals grown at high pressure and high temperature have a low –OH group defect content. After a few millimeters of crystal growth under these conditions, α 3500 reaches 0.1 cm −1 and no free –OH are present. The d 11 value measured on an X-cut from the crystal with x = 0.0375 is 3.08 pC N −1 (±0.15), in good agreement with the value of 2.97 pC N −1 obtained using density functional theory based calculations. Piezoelectric measurements were performed on the Si1− x Ge x O2 crystal with x = 0.0375, both at room temperature and after annealing at various temperatures. The piezoelectric signal of the crystal with x = 0.0375 and pure SiO2 disappears after annealing at 635 °C and 545 °C, respectively. Nonlinear optical (NLO) properties of Si1− x Ge x O2 crystals were measured by Maker's fringe technique on Z-cut χ 11 (2) and their corresponding values for x = 0.023 and 0.028 are 1.3(2) pm V −1 and 1.6(2) pm V −1, respectively. These values are in good agreement with density functional theory based calculations. The light induced damage threshold values measured on Si1− x Ge x O2 crystals with x = 0.023 and 0.028 are very similar to that of α-quartz.