High strength Ni–Zr–(Al) nanoeutectic composites with large plasticity. (August 2015)

• Record Type: Journal Article
• Authors: Maity, T.; Das, J.
• Is Part Of: Intermetallics. Volume 63(2015:Aug.)
• Page Start: 51
• Page End: 58
• Publication Date: 2015-08
• Subjects: A. Intermetallics -- B. Alloy design -- B. Mechanical properties -- B. Nanocrystalline structure -- C. Casting -- D. Microstructure; Intermetallic compounds -- Metallography -- Periodicals; Metallic glasses -- Periodicals; Composés intermétalliques -- Métallographie -- Périodiques; 669.94
• DOI: 10.1016/j.intermet.2015.04.002
• Languages: English
• ISSNs: 0966-9795

Abstract

Abstract: Micrometer-sized γ−Ni dendrite reinforced nanoeutectic matrix composites have been developed in (Ni0.92 Zr0.08 )100– x Al x (0 ≤ x ≤ 4) by arc melting. The eutectic matrix is composed of alternate nano-lamellae of intermetallic Ni5 Zr and fcc–Ni solid solution phases. All these composites exhibit very high strength, large compressive plasticity ∼25% and strain-hardening up to 1780 MPa. Al dissolves in γ−Ni(Zr) solid solution phase, decreases its hardness/strength, and increases the volume % of γ−Ni dendrite from 20% ( x = 0) to 29% ( x = 4). Whereas, refinement of the eutectic lamellae thickness from 275 nm ( x = 0) to 160 nm ( x = 4) increases the matrix hardness and retains the global strength of the composites. The effect of Al addition on the microstructure formation, volume fraction as well as the length scale of the constituent phases, and mechanical properties, have been discussed using an analytical model. Highlights: γ−Ni dendrite-nanoeutectic composites developed in Ni–Zr-(Al) by arc melting. The nanoeutectic matrix composed of alternate lamellae of Ni5 Zr and fcc–Ni phases. Addition of Al refined the lamellar spacing from 275 nm to 160 nm. The composites exhibit high compressive strength (∼1780 MPa) and ∼25% plasticity. The hardness of the composites has been predicted using an analytical model.