The chemical bonding and fire performance of the nylon/cotton blend fabrics treated with a hydroxy-functional organophosphorus oligomer. (June 2016)

• Record Type: Journal Article
• Authors: Chen, Qin; Yang, Charles Q.; Zhao, Tao
• Is Part Of: Polymer degradation and stability. Volume 128(2016:Jun.)
• Page Start: 237
• Page End: 244
• Publication Date: 2016-06
• Subjects: Chemical bonding -- Cotton -- Cotton/nylon blends -- Crosslinked polymeric networks -- Flame retardant finishing -- Flame retarded textiles -- Military protective clothing -- Nylon; Polymers -- Deterioration -- Periodicals; Stabilizing agents -- Periodicals; Polymères -- Dégradation -- Périodiques; Stabilisants -- Périodiques; 668.9
• DOI: 10.1016/j.polymdegradstab.2016.03.014
• Languages: English
• ISSNs: 0141-3910

Abstract

Abstract: Nylon/cotton blend fabrics have long been used in military protective clothing. Because fire risk has drastically increased in recent warfare, developing flame retarded military nylon/cotton fabrics becomes extremely important for protecting military personnel. It was previously discovered that a hydroxy-functional organophosphorus oligomer (HFPO) was bound to a nylon fabric in the presence of dimethyloldihydroxylethyleneurea (DMDHEU) as a bonding agent. In this research, the bonding mechanism of HFPO/DMDHEU on the nylon/cotton blend fabrics was investigated. HFPO was bound to the nylon/cotton blend fabrics by (1) forming HFPO/DMDHEU crosslinked polymeric networks on both nylon and cotton and (2) forming a DMDHEU bridge between cellulose and HFPO on cotton. The relative quantity of the HFPO/DMDHEU crosslinked networks and that of the DMDHEU-bridging formed on the treated blend fabrics was controlled by the HFPO-to-DMDHEU ratio. The HFPO/DMDHEU system was an effective and durable flame retarding treatment system for nylon/cotton military blend fabrics. The treated fabrics passed the fabric vertical burning test after 50 home laundering cycles. The fire performance and hydrolysis-resistance of different nylon/cotton blend fabrics treated with HFPO/DMDHEU was fully evaluated, and the performance data were analyzed in relation with the bonding mechanism.