Role of microstructure on initiation and propagation of fatigue cracks in precipitate strengthened Cu–Ni–Si alloy. (June 2016)

• Record Type: Journal Article
• Authors: Goto, M.; Han, S.Z.; Lim, S.H.; Kitamura, J.; Fujimura, T.; Ahn, J.-H.; Yamamoto, T.; Kim, S.; Lee, J.
• Is Part Of: International journal of fatigue. Volume 87(2016)
• Page Start: 15
• Page End: 21
• Publication Date: 2016-06
• Subjects: Copper alloys -- Fatigue -- Grain boundaries -- Crack initiation -- Ni2Si precipitates; Materials -- Fatigue -- Periodicals; Materials -- Fatigue; Periodicals; 620.1122
• DOI: 10.1016/j.ijfatigue.2016.01.004
• Languages: English
• ISSNs: 0142-1123

Abstract

Highlights: Fatigue cracks originated from GBs, followed by the growth along the slip planes. Heterogeneously precipitated δ-Ni2 Si particles and PFZs were formed around GB areas. The particles/PFZ-induced localized strain was main cause of the crack initiation. There were a small number of DP grains which had negligible effects on fatigue strength. Abstract: Fatigue tests were conducted on round-bar specimens to understand the fatigue behavior of precipitate-strengthened Cu–6Ni–1.5Si alloy. Aging at 500 °C for 0.5 h produced δ-Ni2 Si precipitates in the matrix, homogeneously and heterogeneously precipitated δ-Ni2 Si particles, and a precipitate-free zone around the grain boundaries. The cracks were initiated at the grain boundaries, followed by growth along the crystallographic slip planes in the adjacent grains. Crack propagation from the crack origin along the grain boundaries was occasionally observed. The physical background of fatigue damage is discussed in light of the role of microstructure on the behavior of fatigue cracks.