Selective oxidation of 1, 2-propanediol to lactic acid catalyzed by hydroxyapatite-supported Pd and Pd–Ag nanoparticles. Issue 129 (16th December 2015) - Feng, Yonghai
Abstract : Selective catalytic oxidation of 1, 2-propanediol is an alternative, effective, and environmentally benign method for producing lactic acid. Abstract : Selective catalytic oxidation of 1, 2-propanediol is an alternative, effective, and environmentally benign method for producing lactic acid. Hydroxyapatite-supported Pd (Pd/HAP) and Pd–Ag (Pd–Ag/HAP) catalysts were prepared by the sol-immobilization method. The as-prepared catalysts were characterized by XRD, TEM, HRTEM, XPS, BET, and CO2 -TPD techniques. The average particle sizes of Pd nanocubes in Pd/HAP catalysts were tuned from 6 to 18 nm by changing the amount of KBr and PVP, which significantly affected the 1, 2-propanediol conversion and the lactic acid selectivity. Pd/HAP catalyst with cubic Pd nanoparticles was more selective to lactic acid than Pd/HAP catalyst with spherical Pd nanoparticles in the oxidation of 1, 2-propanediol. The coalesced Pd and Ag nanoparticles in Pd–Ag/HAP bimetallic catalysts synergistically catalyzed the oxidation of 1, 2-propanediol to lactic acid. The support HAP with high basicity promoted the oxidation of 1, 2-propanediol to lactic acid. When the catalytic oxidation of 1, 2-propanediol with O2 was carried out at 100 °C for 2 h in an alkaline solution, the lactic acid selectivity was 86.2% at the 1, 2-propanediol conversion of 96.2% over Pd2 /HAP-6 catalyst while the lactic acid selectivity was 88.8% at the 1, 2-propanediol conversion of 86.3% over Pd1 Ag1 /HAP catalyst. The activation energies for the catalytic oxidation of 1, 2-propanediol were in the order of E a (Pd1 Ag1 /HAP) < E a (Pd2 /HAP-6) < E a Ag2 /HAP.