Effect of strain-rate on the deformation response of D03-ordered Fe3Al. (15th January 2016)

• Record Type: Journal Article
• Authors: Janda, D.; Ghassemi-Armaki, H.; Bruder, E.; Hockauf, M.; Heilmaier, M.; Kumar, K.S.
• Is Part Of: Acta materialia. Volume 103(2016)
• Page Start: 909
• Page End: 918
• Publication Date: 2016-01-15
• Subjects: Iron aluminide -- Strain rate -- Shear localization -- Twinning -- Work-hardening; Materials -- Periodicals; Materials science -- Periodicals; Materials -- Mechanical properties -- Periodicals; Metallurgy -- Periodicals; Chemistry, Inorganic -- Periodicals; 620.112
• DOI: 10.1016/j.actamat.2015.11.002
• Languages: English
• ISSNs: 1359-6454

Abstract

Abstract: The mechanical response of centrifugally cast Fe3 Al with the composition Fe–27Al (at.%) containing micro-alloying additions of Nb, Zr, C, and B was investigated over a wide range of strain rates between 10 −4 and 10 3 s −1 at room temperature. Tests were carried out in compression using a (i) screw-driven load frame, (ii) drop impact tester, and (iii) split-Hopkinson pressure bar at quasi-static, intermediate and dynamic strain rates respectively. Post deformation analysis was carried out by DSC, SEM/EBSD, TEM and micropillar deformation. In all instances, the stress-strain curves show initial hardening (∼first 5% plastic strain) followed by a plateau in stress. A loss in work-hardening occurs at the highest strain rates examined (>10 3 s −1 ) and is likely associated with shear localization; in addition, (2 1 ¯ 1 ) [11 1 ¯ ]-type twinning was observed at these high strain rates at room temperature. This observation is in line with previous theoretical calculations of the antiphase boundary (APB) energy. The consequence of a continuously increasing yield stress with strain rate and a loss in work hardening at the highest strain rates together yields a maximum in flow stress at the intermediate strain rate. Graphical abstract: