Stochastic modelling of perfect inspection and repair actions for leak–failure prone internal corroded pipelines. (February 2016)

• Record Type: Journal Article
• Authors: Ossai, Chinedu I.; Boswell, Brian; Davies, Ian J.
• Is Part Of: Engineering failure analysis. Volume 60(2016:Feb.)
• Page Start: 40
• Page End: 56
• Publication Date: 2016-02
• Subjects: Markov modelling -- Lifecycle phases -- Weibull distribution -- Failure probability -- Inspection and repair cost -- Corrosion wastage time; System failures (Engineering) -- Periodicals; Fracture mechanics -- Periodicals; Reliability (Engineering) -- Periodicals; Pannes -- Périodiques; Rupture, Mécanique de la -- Périodiques; Fiabilité -- Périodiques; Fracture mechanics; Reliability (Engineering); System failures (Engineering); Periodicals; Electronic journals; 620.112
• DOI: 10.1016/j.engfailanal.2015.11.030
• Languages: English
• ISSNs: 1350-6307

Abstract

Abstract: To enhance the performance of any facility, reduce cost and failure probability involves proper inspection and repair decisions. To be able to establish the cost of repair and inspection of corroded pipelines at different stages of the corrosion defect depth growth, Markov modelling technique was adopted. This model formulated an inspection and repair technique, which has the potentials of aiding policy makers in maintenance management of internally corroded pipelines. The transition states were determined using the Remaining Useful Life (RUL) of the pipelines whilst Weibull distribution was used for calculating the corrosion wastage rates at the lifecycle transition phases. Monte Carlo simulation and degradation models were applied for determining future corrosion defect depth growth, in a bid to establish periodic inspection and repair procedures and their costs. Data from an onshore pipeline inspected with Magnetic Flux Leakage (MFL) in-Line-Inspection (ILI) technique was used to test the validity of the model. The results obtained indicate that the model has practical applications for inspection and repairs of aged-internally corroded pipelines. Highlights: Modelled inspection and repair of corroded pipeline using Markov process Expressed the transition states as a function of retained pipe-wall thickness Inspection and repair on the pipeline depended on the corroded depth. Monte Carlo simulation was used to predict the time of corrosion wastage.