Paraffin/expanded vermiculite composite phase change material as aggregate for developing lightweight thermal energy storage cement-based composites. (15th December 2015)

• Record Type: Journal Article
• Authors: Xu, Biwan; Ma, Hongyan; Lu, Zeyu; Li, Zongjin
• Is Part Of: Applied energy. Volume 160(2015:Dec. 15)
• Page Start: 358
• Page End: 367
• Publication Date: 2015-12-15
• Subjects: Paraffin -- Expanded vermiculite -- Phase change material -- Thermal energy storage -- Lightweight cement-based composite; Power (Mechanics) -- Periodicals; Energy conservation -- Periodicals; Energy conversion -- Periodicals; 621.042
• DOI: 10.1016/j.apenergy.2015.09.069
• Languages: English
• ISSNs: 0306-2619

Abstract

Highlights: The composite PCM has onset melting temperature 27.0 °C and latent heat 77.6 J/g. LW-TESCCs with the composite PCM were made with bulk densities below 1500 kg/m 3 . LW-TESCCs reveal superior thermal insulation performance and heat storage merit. Abstract: In this study, a new paraffin/expanded vermiculite composite phase change material (PCM) was tailor-made as aggregate for developing lightweight thermal energy storage cement-based composites (LW-TESCCs). Vermiculite calcined at 800 °C for 1 h (EVM-800) can be considered as the optimum paraffin supporting matrix candidate, as it has the best expanded microstructure and crystallization. The composite PCM was fabricated at a paraffin-to-EVM-800 weight ratio of 0.6:1.0 by the vacuum impregnation method. The results of scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR) show that the paraffin can be well vacuum drawn into the expanded interlayer spaces of EVM-800, and that the paraffin and EVM-800 are chemically inert. The differential scanning calorimetry (DSC) results reveal that the composite PCM has an onset melting temperature of 27.0 ± 0.1 °C and latent heat of 77.6 ± 4.3 J/g, and good thermal stability is clearly suggested by the thermogravimetric analysis (TGA) results. Moreover, the LW-TESCCs with bulk densities below 1500 kg/m 3 were further developed by incorporating the composite PCM as sand replacement. It is found that the LW-TESCCs have significantly improved thermal resistance performance and well-endowed thermal storage capabilities. Thus, it can be expected that the potential applications of the LW-TESCCs in building envelopes would significantly contribute to reducing indoor air temperature fluctuations and in saving energy.