Mechanical properties study of micro‐ and nano‐hydroxyapatite reinforced ultrahigh molecular weight polyethylene composites. Issue 3 (26th September 2015)

• Record Type: Journal Article
• Authors: Kang, Xueqin; Zhang, Wei; Yang, Chunmin
• Is Part Of: Journal of applied polymer science. Volume 133:Issue 3(2016)
• Page Start: n/a
• Page End: n/a
• Publication Date: 2015-09-26
• Subjects: Polymers -- Periodicals; Polymerization -- Periodicals; 668.9
• DOI: 10.1002/app.42869
• Languages: English
• ISSNs: 0021-8995

Abstract

<abstract abstract-type="main"> <title>ABSTRACT</title> <p>This is a comparative study between ultrahigh molecular weight polyethylene (UHMWPE) reinforced with micro‐ and nano‐hydroxyapatite (HA) under different filler content. The micro‐ and nano‐HA/UHMWPE composites were prepared by hot‐pressing method, and then compression strength, ball indentation hardness, creep resistance, friction, and wear properties were investigated. To explore mechanisms of these properties, differential scanning calorimetry, infrared spectrum, wettability, and scanning electron microscopy with energy dispersive spectrometry analysis were carried out on the samples. The results demonstrated that UHMWPE reinforced with micro‐ and nano‐HA would improve the ball indentation hardness, compression strength, creep resistance, wettability, and wear behavior. The mechanical properties for both micro‐ and nano‐HA/UHMWPE composites were comparable with pure UHMWPE. The mechanical properties of nano‐HA/UHMWPE composites are better compared with micro‐HA/UHMWPE composites and pure UHMWPE. The optimum filler quantity of micro‐ and nano‐HA/UHMWPE composites is found to be at 15 wt % and 10 wt %, separately. The micro‐ and nano‐HA/UHMWPE composites exhibit a low friction coefficient and good wear resistance at this content. The worn surface of HA/UHMWPE composites shows the wear mechanisms changed from furrow and scratch to surface rupture and delamination when the weight percent of micro‐ and nano‐HA exceed 15 wt % and 10 wt %. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. <bold>2016</bold>, <italic>133</italic>, 42869.</p> </abstract>