Microstructural sintering evolution and sintering parameters optimization of the silica-doped Nd:YAG ceramics using the co-precipitated raw powder. Issue 8 (August 2015)

• Record Type: Journal Article
• Authors: Ma, Benyuan; Lu, Tiecheng; Zhang, Wei; Wei, Nian; Lu, Zhongwen; Chen, Xingtao; Shi, Yanli
• Is Part Of: Journal of the European Ceramic Society. Volume 35:Issue 8(2015:Aug.)
• Page Start: 2403
• Page End: 2412
• Publication Date: 2015-08
• Subjects: Ceramic materials -- Periodicals; Composite materials -- Periodicals; Matériaux céramiques -- Périodiques; Composites -- Périodiques; Ceramic materials; Composite materials; Periodicals; Electronic journals; 666.05
• DOI: 10.1016/j.jeurceramsoc.2015.02.003
• Languages: English
• ISSNs: 0955-2219

Abstract

<abstract abstract-type="author" id="abs0005"> <title id="sect0005">Abstract</title> <sec> <p id="spar0005">Using the co-precipitated Nd:YAG raw powder, combined with 0.14 wt.% SiO₂ as sintering aid, the green compacts were vacuum sintered from 1250 to 1750 °C to track the microstructural evolution during ceramic sintering process. The SEM results showed that a silicon-related liquid-phase sintering (1400–1550 °C) could greatly promote the densification process of ceramics with the ceramics at 1550 °C becoming translucent. Based on the evolution results, the parameters of sintering schedule, especially intermediate temperature holds and heating rates, were changed and optimized. The corresponding SEM morphologies and the influence mechanism were investigated. The results revealed that intermediate temperature holds (1250, 1450 and 1600 °C) and slower heating rates (1–5 °C/min) had a significant role in the pore elimination, the fine microstructure of ceramic and the promotion of ceramic transmittance. Using the optimized sintering schedule, a ceramic with fine microstructure could be obtained with a transmittance of 83.8% at 1064 nm.</p> </sec> </abstract>