Oxidation behaviours of electron beam physical vapour deposition fabricated microcrystalline Ni–23·5Cr–2·66Co–1·44Al superalloy sheet at 1000°C. (May 2015)

• Record Type: Journal Article
• Authors: Gang, Z.; Mingwei, L.; Yesheng, Z.; Xiu, L.; Fei, H.; Xiaodong, H.
• Is Part Of: Materials research innovations. Volume 19:Number 5(2015)
• Page Start: S5-959
• Page End: S5-963
• Publication Date: 2015-05
• Subjects: Materials -- Research -- Periodicals; Matériaux -- Recherche -- Périodiques; 620.1105
• DOI: 10.1179/1432891714Z.0000000001229
• Languages: German
• ISSNs: 1432-8917

Abstract

<abstract> <title> <x content-type="archive" xml:space="preserve">Abstract</x> </title> <p>Isothermal oxidation of as-deposited microcrystalline Ni–23·5Cr–2·66Co–1·44Al (wt-%) alloy sheet fabricated by electron beam physical vapour deposition exposed at 1000°C in air up to 100 hours was investigated. Surfaces and cross-sections of the oxidised specimens were studied by scanning electron microscopy. Phase identification of the oxide scale was performed by glancing angle X-ray diffraction. The results indicated that the oxidation kinetics of the alloy sheet obeyed an approximate cubical power law at the early stage of exposure and approximate fourth power law for long oxidation terms. It was found that the oxide scales consisted mainly of an outer Cr₂O₃ oxide layer, and an inner NiO and NiCr₂O₄ mixed oxides layers. An Al₂O₃ layer was formed at the scale/substrate interface after a long-time oxidation. This showed that the outward diffusion rate of Cr atoms was higher than that of Ni atoms and Al atoms.</p> </abstract>