Cyclic oxidation behaviour of as-deposited Ni-11·5Cr-4·5Co-0·5Al superalloy sheet when heated at 800°C. (May 2015)

• Record Type: Journal Article
• Authors: Zongjing, H.; Mingwei, L.; Gang, Z.; Xiu, L.; Yesheng, Z.; Fe, H.; Xiaodong, H.
• Is Part Of: Materials research innovations. Volume 19:Number 5(2015)
• Page Start: S5-186
• Page End: S5-189
• Publication Date: 2015-05
• Subjects: Materials -- Research -- Periodicals; Matériaux -- Recherche -- Périodiques; 620.1105
• DOI: 10.1179/1432891714Z.0000000001073
• Languages: German
• ISSNs: 1432-8917

Abstract

<abstract> <title> <x content-type="archive" xml:space="preserve">Abstract</x> </title> <p>The excellent performance of superalloys is famous for their applications under high-temperature oxidation conditions. The grain size of the superalloy affects the morphology and the composition of the oxide scale. The cyclic oxidation characteristics up to 24 times of Ni-11·5Cr-4·5Co-0·5Al microcrystalline sheets, which are prepared by electron beam physical vapour deposition, were investigated at 800°C in air for 2 hours in this paper. The oxide scales were examined by scanning electron microscopy equipped with an energy-dispersive X-ray system. The oxide scales chemical phase was determined by glancing angle X-ray diffraction. The results showed that the oxide scales were mainly composed of alumina. The surface of the scale was rough and non-uniform with grey and bright zones at the fourth cycle. It became smooth, continuous and uniform at the 24th cycle.</p> </abstract>