Synthesis and swelling properties of a pH‐ and temperature‐dual responsive hydrogel by inverse microemulsion polymerization. Issue 26 (13th March 2015) - Wan, Tao
ABSTRACT A novel pH‐ and temperature‐dual responsive hydrogel was synthesized by inverse microemulsion polymerization, using itonic acid (IA) as pH‐responsive monomer, N‐isopropylacrylamide (NPAM) as thermo‐responsive monomer and acrylamide (AM) as the nonionic hydrophilic monomer. Factors affecting water and salt absorption, as well as swellability of the dual responsive hydrogels, such as IA/NPAM mass ratio and crosslinker amount, were investigated. pH‐ and temperature‐sensitivity and dynamic viscoelasticity behaviors of the dual responsive hydrogels were also studied. The dual responsive responsive hydrogels showed suitable water and salt absorbency, remarkable pH‐, and temperature‐sensitivity, adjustable swellability and enhanced viscoelastic behaviors under high stress. Water absorbency and pH‐sensitivity increased while salt absorbency and temperature‐ sensitivity decreased with increasing IA/NIPAM mass ratio. Both water absorbency and salt absorbency increased first with crosslinker amount increased to 0.2 wt %, and then decreased with increasing crosslinker amount. Temperature‐induced shrinkage range of the dual responsive hydrogels was higher and broader than that of the conventional poly(N‐isopropylacrylamide) hydrogel. TEM indicated that the as‐synthesized hydrogel particles were regular and spherical‐like in shape and had the mean particle size of 49nm in the range of 30–78 nm. FTIR indicated the structure of the dual responsive hydrogels. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 42139.