Production and characterisation of mechanical properties of Ti–Nb–Ta–Mn alloys foams for biomedical applications. (31st March 2015)

• Record Type: Journal Article
• Authors: Guerra, C.; Aguilar, C.; Guzmán, D.; Arancibia, M.; Rojas, P. A.; Lascano, S.; Perez, L.
• Is Part Of: Powder metallurgy. Volume 58:Number 1(2015)
• Page Start: 12
• Page End: 15
• Publication Date: 2015-03-31
• Subjects: Powder metallurgy -- Periodicals; 671.3705
• DOI: 10.1179/0032589914Z.000000000211
• Languages: English
• ISSNs: 0032-5899

Abstract

<abstract> <title> <x content-type="archive" xml:space="preserve">Abstract</x> </title> <p>Development of titanium foams with low Young's modulus as a potential implant material has attracted significant attention. In this work, the effect of manganese on the mechanical properties in compression of Ti–13Ta–30Nb–<italic>x</italic>Mn foams (<italic>x</italic> = 2–6 wt-%) has been studied. Titanium based alloys produced by mechanical alloying were processed to obtain foams using ammonium hydrogen carbonate with a mean particle size of 35 μm (50% v/v) as a space-holder. Powders and space-holder were mixed and uniaxially pressed to form compacts. The space holder was removed by heating the green compacts to 180°C for 1.5 h before sintering at 1300°C for 4 h in Ar. The Young's modulus of the foam was lower than that of pure Ti, and the yield strength increased with the Mn addition. The Gibson–Ashby, Meyer and Nielsen models were applied to predict the mechanical properties of the titanium foams.</p> </abstract>