Effect of High‐Energy Ball Milling and Silica Fume Addition in BaCO3–Al2O3. Part I: Formation of Cementing Phases. Issue 12 (4th August 2014)

• Record Type: Journal Article
• Authors: Kumar, Pattem Hemanth; Srivastava, Abhinav; Kumar, Vijay; Kumar, Pradeep; Singh, Vinay Kumar; Rigaud, M.
• Is Part Of: Journal of the American Ceramic Society. Volume 97:Issue 12(2014)
• Page Start: 3755
• Page End: 3763
• Publication Date: 2014-08-04
• Subjects: Ceramics -- Periodicals; 620.1405
• DOI: 10.1111/jace.13173
• Languages: English
• ISSNs: 0002-7820

Abstract

<abstract abstract-type="main" id="jace13173-abs-0001"> <title> <x xml:space="preserve">Abstract</x> </title> <p>The effects of high‐energy ball milling and subsequent calcination on the formation of barium aluminate cementing phases using mixtures of Al₂O₃ and BaCO₃ were investigated. Silica fume was further added in the raw mixtures to observe its role on the cementing phase formation. Results indicated that the decomposition temperature of BaCO₃ lowered remarkably with the increase in milling time. Barium aluminate cements with grain size in nanometer range were obtained from high‐energy ball‐milled raw mixtures. X‐ray diffraction (XRD) results confirmed several crystalline barium‐silicate and barium aluminate phases present. Formation of crystalline BaO·Al₂O₃ phase was observed between 1000°C and 1100°C in the raw mixtures, which were obtained in amorphous state after milling for 5 h. This temperature is at least 300°C lower than that used in the traditional solid‐state method. Fume SiO₂ additions resulted in BaO·Al₂O₃·2SiO₂ (celsian) formation which acted as a retarder, provides more workability and mechanical strength.</p> </abstract>