One-dimensional TiO2 nanotubes arrays: Influence of anodisation voltage and their photocatalytic activity performance. (8th December 2014)

• Record Type: Journal Article
• Authors: Lee, W. H.; Lai, C. W.; Lim, Y. S.; Hamid, S. B. A.
• Is Part Of: Materials research innovations. Volume 18:Number 6(2014)
• Page Start: S6-474
• Page End: S6-476
• Publication Date: 2014-12-08
• Subjects: Materials -- Research -- Periodicals; Matériaux -- Recherche -- Périodiques; 620.1105
• DOI: 10.1179/1432891714Z.0000000001001
• Languages: English
• ISSNs: 1432-8917

Abstract

<abstract> <title> <x content-type="archive" xml:space="preserve">Abstract</x> </title> <p>A systematic study of titanium dioxide (TiO₂) nanotube arrays grown by electrochemical anodisation in an ethylene glycol electrolyte containing 0·5 wt-% ammonium fluoride has been carried out, with a range of anodisation voltage of 15–60 V for 1 hour. Among all of the applied anodisation voltages, 60 V resulted in the highest aspect ratio TiO₂ nanotube arrays with the tube length of approximately 2 μm and pore size of 105 nm. The diameter and length of nanotubes were found to be increased with anodisation voltage because of the high electric field dissolution at the barrier layer of nanotubes. Besides, the anatase phase of TiO₂ could be detected from the X-ray diffraction patterns after subjecting the annealing process at 400°C in argon atmosphere for 4 hours. Based on the photocatalytic studies, it was observed that TiO₂ nanotube arrays with the highest aspect ratio (length/pore's size) exhibited preferably high photocatalytic activity among the samples owing to the larger active surface area to generate more photo-induced electron–hole pairs. This condition will enhance the photocatalytic degradation efficiency of methyl orange.</p> </abstract>