Fabrication and Dielectric Properties of Ba0.63Sr0.37TiO3 Thin Films on SiC Substrates. Issue 10 (6th September 2014)

• Record Type: Journal Article
• Authors: Song, Lirong; Chen, Ying; Wang, Genshui; Yang, Lihui; Ge, Jun; Dong, Xianlin; Xiang, Pinghua; Zhang, Yuanyuan; Tang, Xiaodong; Akdogan, E. K.
• Is Part Of: Journal of the American Ceramic Society. Volume 97:Issue 10(2014)
• Page Start: 3048
• Page End: 3051
• Publication Date: 2014-09-06
• Subjects: Ceramics -- Periodicals; 620.1405
• DOI: 10.1111/jace.13218
• Languages: English
• ISSNs: 0002-7820

Abstract

<abstract abstract-type="main" id="jace13218-abs-0001"> <title> <x xml:space="preserve">Abstract</x> </title> <p>Ba_0.63Sr_0.37TiO₃ (BST) films were first deposited on SiC substrates with LNO bottom electrodes by magnetron sputtering. The BST/LNO/SiC thin films exhibit high dielectric tunability and low dielectric loss while maintaining excellent temperature coefficient of dielectric constant in the temperature range between 250 and 350 K. We also investigated the effect of film thickness on the dielectric properties. BST(430 nm)/LNO/SiC film has higher tunability (68.09% @700 kV/cm), lower loss tangent (tanδ = 0.00987) and quite a bit higher figure of merit (FOM = 68.99) as compared with that of BST(300 nm)/LNO/SiC film. Our results demonstrate that combining ferroelectric BST films with SiC substrates is very promising for the development of tunable devices over a large temperature range.</p> </abstract>