Zirconium Diboride with High Thermal Conductivity. Issue 6 (12th May 2014)

• Record Type: Journal Article
• Authors: Lonergan, Jason M.; Fahrenholtz, William G.; Hilmas, Greg E.; Trice, R.
• Is Part Of: Journal of the American Ceramic Society. Volume 97:Issue 6(2014)
• Page Start: 1689
• Page End: 1691
• Publication Date: 2014-05-12
• Subjects: Ceramics -- Periodicals; 620.1405
• DOI: 10.1111/jace.12950
• Languages: English
• ISSNs: 0002-7820

Abstract

<abstract abstract-type="main" id="jace12950-abs-0001"> <title> <x xml:space="preserve">Abstract</x> </title> <p>Thermal properties were characterized for zirconium diboride produced by reactive hot pressing and compared to ZrB₂ ceramics that were hot pressed from commercial powders. No sintering additives were used in either process. Thermal conductivity was calculated from measured values of heat capacity, thermal diffusivity, and density for temperatures ranging from 298 to 2273 K. ZrB₂ produced by reactive hot pressing achieved near full density, but had a small volume fraction of ZrO₂, whereas hot‐pressed ZrB₂ contained porosity and carbon inclusions. Reactive hot pressing produced a ceramic with higher thermal diffusivity and heat capacity, resulting in thermal conductivities of 127 W·(m·K)⁻¹ at 298 K and 80 W·(m·K)⁻¹ at 2273 K, which were up to ~30% higher than typically reported for hot‐pressed ZrB₂.</p> </abstract>