Multifunctional polyimide/graphene oxide composites via in situ polymerization. Issue 9 (5th December 2013) - Zhu, Jiadeng
ABSTRACT In this article, we detail an effective way to improve electrical, thermal, and gas barrier properties using a simple processing method for polymer composites. Graphene oxide (GO) prepared with graphite using a modified Hummers method was used as a nanofiller for r‐GO/PI composites by in situ polymerization. PI composites with different loadings of GO were prepared by the thermal imidization of polyamic acid (PAA)/GO. This method greatly improved the electrical properties of the r‐GO/PI composites compared with pure PI due to the electrical percolation networks of reduced graphene oxide within the films. The conductivity of r‐GO/PI composites (30:70 w/w) equaled 1.1 × 101 S m−1, roughly 1014 times that of pure PI and the oxygen transmission rate (OTR, 30:70 w/w) was reduced by about 93%. The Young's modulus of the r‐GO/PI composite film containing 30 wt % GO increased to 4.2 GPa, which was an approximate improvement of 282% compared with pure PI film. The corresponding strength and the elongation at break decreased to 70.0 MPa and 2.2%, respectively. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014, 131, 40177.