High‐density remote plasma sputtering of high‐dielectric‐constant amorphous hafnium oxide films. Issue 5 (4th March 2013) - Li, Flora M.
Abstract Hafnium oxide (HfOx) is a high dielectric constant (k) oxide which has been identified as being suitable for use as the gate dielectric in thin film transistors (TFTs). Amorphous materials are preferred for a gate dielectric, but it has been an ongoing challenge to produce amorphous HfOx while maintaining a high dielectric constant. A technique called high target utilization sputtering (HiTUS) is demonstrated to be capable of depositing high‐k amorphous HfOx thin films at room temperature. The plasma is generated in a remote chamber, allowing higher rate deposition of films with minimal ion damage. Compared to a conventional sputtering system, the HiTUS technique allows finer control of the thin film microstructure. Using a conventional reactive rf magnetron sputtering technique, monoclinic nanocrystalline HfOx thin films have been deposited at a rate of ∼1.6 nm min−1 at room temperature, with a resistivity of 1013 Ω cm, a breakdown strength of 3.5 MV cm−1 and a dielectric constant of ∼18.2. By comparison, using the HiTUS process, amorphous HfOx (x = 2.1) thin films which appear to have a cubic‐like short‐range order have been deposited at a high deposition rate of ∼25 nm min−1 with a high resistivity of 1014 Ω cm, a breakdown strength of 3 MV cm−1 and a high dielectric constant of ∼30. Two key conditions must be satisfied in the HiTUS system for high‐k HfOx to be produced. Firstly, the correct oxygen flow rate is required for a given sputtering rate from the metallic target. Secondly, there must be an absence of energetic oxygen ion bombardment to maintain an amorphous microstructure and a high flux of medium energy species emitted from the metallic sputtering target to induce a cubic‐like short range order. This HfOx is very attractive as a dielectric material for large‐area electronic applications on flexible substrates.